Microstructural stability of a self-ion irradiated lanthana-bearing nanostructured ferritic steel

Type
Journal Article
Year of Publication
2015
Authors
Somayeh Pasebani
Indrajit Charit
Jatuporn Burns
Sultan Alsagabi
Darryl P. Butt
James I. Cole
Lloyd M. Price
Lin Shao
Journal
NUMA Journal of Nuclear Materials
Volume
462
ISSN
0022-3115
Date Published
Jan. 1, 2015
Abstract

The first ever study of ion irradiation in a lanthana-bearing NFS. The NFS was produced using mechanical alloying and spark plasma sintering. Irradiation with Fe2+ ions up to 100 dpa at two temperatures. TEM and APT performed to understand the changes in nanofeatures. Nanohardness related with microstructural changes due to irradiation.Thermally stable nanofeatures with high number density are expected to impart excellent high temperature strength and irradiation stability in nanostructured ferritic steels (NFSs) which have potential applications in advanced nuclear reactors. A lanthana-bearing NFS (14LMT) developed via mechanical alloying and spark plasma sintering was used in this study. The sintered samples were irradiated by Fe2+ ions to 10, 50 and 100 dpa at 30 °C and 500 °C. Microstructural and mechanical characteristics of the irradiated samples were studied using different microscopy techniques and nanoindentation, respectively. Overall morphology and number density of the nanofeatures remained unchanged after irradiation. Average radius of nanofeatures in the irradiated sample (100 dpa at 500 °C) was slightly reduced. A notable level of irradiation hardening and enhanced dislocation activity occurred after ion irradiation except at 30 °C and 50 dpa. Other microstructural features like grain boundaries and high density of dislocations also provided defect sinks to assist in defect removal.